镍及镍合金带材力学性能(GB2072-80)
镍及镍合金管材力学性能(GB2882-81)
镍及镍铜合金棒材室温纵向力学性能(GB4435-84)
镍及镍合金线性能(GB3113、3120、3121-82)
加工镍及镍合金牌号及化学成份(GB5235-85)
镍及镍合金带材力学性能(GB2072-80)
牌号
|
状态
|
抗拉强度,N/m㎡,不小于
|
伸长率,%,不小于
|
N6、N7、MSi0.19
NSi0.2、NMg0.1
|
M
Y
|
392
539
|
30
2
|
NCu28-2.5-1.5
|
M
Y2
|
441
568
|
2.5
6.5
|
|
镍及镍合金管材力学性能(GB2882-81)
牌号
|
状态
|
抗拉强度,N/m㎡,不小于
|
伸长率,%,不小于
|
N6
|
M
Y
|
373
520
|
35
5
|
NCu28-2.5-1.5
NCu40-2-1
|
M
Y
|
441
569
|
20
2
|
|
镍及镍铜合金棒材室温纵向力学性能(GB4435-84)
牌号
|
状态
|
直径,mm
|
抗拉强度,N/m㎡
|
伸长率,%
|
不 小 于
|
N6
|
Y
|
5-20
﹥20-30
﹥30-40
|
588
539
510
|
5
6
6
|
M
|
50-30
﹥30-40
|
392
343
|
30
30
|
R
|
32-50
﹥50-60
|
343
343
|
25
20
|
NCu28-2.5-1.5
|
Y
|
5-15
﹥15-30
﹥30-40
|
667
637
588
|
4
6
6
|
Y2
|
5-20
﹥20-30
|
588
539
|
10
12
|
M
|
5-30
﹥30-40
|
441
441
|
20
20
|
R
|
32-60
|
392
|
25
|
NCu40-2-1
|
Y
|
50-20
﹥20-30
|
637
588
|
4
5
|
M
|
5-30
|
392
|
25
|
R
|
32-50
|
实测
|
实测
|
|
镍及镍合金线性能(GB3113、3120、3121-82)
牌号
|
状态
|
直径,mm
|
抗拉强度,N/m㎡,不小于
|
伸长率,%,不小于
|
N4
|
M
|
0.03-0.20
0.21-0.48
0.50-1.00
1.05-6.00
|
373
343
314
294
|
15
20
20
25
|
Y2
|
0.10-0.50
0.53-1.00
1.05-5.00
|
686-883
588-785
490-637
|
-
-
-
|
Y
|
0.03-0.09
0.10-0.50
0.53-1.00
1.05-6.00
|
785-1275
735-981
686-883
539-834
|
-
-
-
|
N6
N7
N8
|
M
|
0.03-0.20
0.21-0.48
0.50-1.00
1.05-6.00
|
422
392
373
343
|
15
20
20
25
|
Y2
|
0.10-0.50
0.53-1.00
1.05-5.00
|
785-981
686-834
539-686
|
-
-
-
|
Y
|
0.03-0.09
0.10-0.50
0.53-1.00
1.05-6.00
|
883-1325
834-1079
735-981
637-883
|
-
-
-
-
|
NCu28-2.5-1.5
|
M
|
0.05-0.50﹥0.50-4.0﹥4.0-6.0
|
471
451
441
|
15
25
30
|
Y
|
0.05-0.50﹥0.50-4.0﹥4.0-6.0
|
785-981
686-883
637-834
|
-
-
-
|
NCu40-2-1
|
M
|
0.1-6.0
|
441
|
实测
|
Y
|
0.1-6.0
|
637
|
实测
|
DN
NSi0.19
NMg0.1
DNMg0.06
|
M
|
0.03-0.20
0.21-0.48
0.50-1.00
1.05-6.00
|
422
392
373
343
|
15
20
20
25
|
Y2
|
0.10-0.50
0.53-1.00
1.05-5.00
|
785-981
686-834
539-686
|
-
-
-
|
Y
|
0.03-0.09
0.10-0.50
0.53-1.00
1.05-6.00
|
883-1275
834-1079
735-981
637-883
|
-
-
-
-
|
|
加工镍及镍合金牌号及化学成份(GB5235-85)
牌号
|
化 学 成 份 , % ( 质 量 )
|
Ni+Co
不小于
|
Cu
|
Si
|
Mn
|
C
|
Mg
|
S
|
P
|
Fe
|
Pb
|
Bi
|
As
|
Sb
|
Zn
|
Cd
|
Sn
|
|
杂质总和
|
N2
|
99.98
|
.001
|
.003
|
.002
|
.005
|
.003
|
.001
|
.001
|
.007
|
.0003
|
.0003
|
.001
|
.0003
|
.002
|
.0003
|
.001
|
|
.02
|
N4
|
99.9
|
.015
|
.03
|
.002
|
.01
|
.01
|
.001
|
.001
|
.04
|
.001
|
.001
|
.001
|
.001
|
.005
|
.001
|
.001
|
|
.1
|
N6
|
99.5
|
.06
|
.10
|
.05
|
.10
|
.10
|
.005
|
.002
|
.10
|
.002
|
.002
|
.002
|
.002
|
.007
|
.002
|
.002
|
|
.5
|
N8
|
99.0
|
.15
|
.15
|
.20
|
.20
|
.10
|
.015
|
-
|
.30
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
1.0
|
DN
|
99.35
|
.06
|
.02-.10
|
.05
|
.02-.10
|
.02-.10
|
.005
|
.002
|
.10
|
.002
|
.002
|
.002
|
.002
|
.007
|
.002
|
.002
|
|
.35
|
NY1
|
99.7
|
.1
|
.10
|
-
|
.02
|
.10
|
.005
|
-
|
.10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
.3
|
NY2
|
99.4
|
.01-.10
|
.10
|
-
|
-
|
-
|
.002-.01
|
-
|
.10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
O:.03-.3
|
.6
|
NY3
|
99.0
|
.15
|
.2
|
-
|
.1
|
.10
|
.005
|
-
|
.25
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
1.0
|
NMn3
|
余量
|
.50
|
.30
|
2.30-3.30
|
.30
|
.10
|
.03
|
.010
|
.65
|
.002
|
.002
|
.030
|
.002
|
-
|
-
|
-
|
|
1.5
|
NMn5
|
余量
|
.50
|
.30
|
4.60-5.40
|
.30
|
.10
|
.03
|
.020
|
.65
|
.002
|
.002
|
.030
|
.002
|
-
|
-
|
-
|
|
2.0
|
NCu40-2-1
|
余量
|
38.0-42.0
|
.15
|
1.25-2.25
|
.30
|
-
|
.02
|
.005
|
.2-1.0
|
.006
|
-
|
-
|
-
|
-
|
-
|
-
|
|
.6
|
NCu28-2.5-1.5
|
余量
|
27.0-29.0
|
.10
|
1.2-1.8
|
.20
|
.10
|
.02
|
.005
|
2.0-3.0
|
.003
|
.002
|
.010
|
.002
|
-
|
-
|
-
|
|
.6
|
NMg0.1
|
99.6
|
.05
|
.02
|
.05
|
.05
|
.07-.15
|
.005
|
.002
|
.07
|
.002
|
.002
|
.002
|
.002
|
.007
|
.002
|
.002
|
|
.40
|
NSi0.19
|
99.4
|
.05
|
.15-.25
|
.05
|
.10
|
.05
|
.005
|
.002
|
.07
|
.002
|
.002
|
.002
|
.002
|
.007
|
.002
|
.002
|
|
.50
|
NW4-0.15
|
余量
|
.02
|
.01
|
.005
|
.01
|
.01
|
.003
|
.002
|
.03
|
.002
|
.002
|
.002
|
.002
|
.003
|
.002
|
.002
|
Al.01,W3.0-4.0,Ca.07-.17
|
.15
|
NW4-0.1
|
余量
|
.005
|
.005
|
.005
|
.01
|
.005
|
.001
|
.001
|
.03
|
.001
|
.001
|
-
|
.001
|
.003
|
.001
|
.001
|
Al.005,W3.0-4.0,Zr.08-.14,Ti.005
|
.12
|
MW4-0.07
|
余量
|
.02
|
.01
|
.005
|
.01
|
.05-.1
|
.001
|
.002
|
.03
|
.002
|
.002
|
.002
|
.002
|
.005
|
.002
|
.002
|
Al.001,W3.5-4.5
|
.2
|
NiSi3
|
余量
|
-
|
2-3
|
.05-.07
|
.05
|
-
|
.02
|
.002
|
.10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
Co.05-.6
|
-
|
NCr10
|
余量
|
-
|
.05-.06
|
.01-.2
|
.05
|
-
|
.02
|
.002
|
.10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
Cr9.0-10.0 Co.1-1.2
|
|
|
|